Polyurethane rollers

Automotive roller beds conveying system is widely used in automobile production plant: Weld , Paint and Assembly Line. The growing competitive in automobile industry requires more effective production line with continuous running time. This demands the rollers quality to be more reliable, wear-resistance and concentricity. Roller tables can be chain driven or belt driven ( for noiseless and clean operation) with a wide variety of rollers made from steel, stainless steel, polyurethane, etc.Easy to integrate with lifters, cross transfers, swivel table, turntables and other devices to form an integrated layout.
High performance elastomer polyurethane, choose high-end raw materials imported from the industry;

Excellent chemical resistance to solvents, petroleum products and other materials.

Working temperature (-30 deg.C to 100+ deg. C depending on formulation)

Capable of handling 1500-5000kgs

Description

Product Features

Automotive roller beds conveying system is widely used in automobile production plant: Weld , Paint and Assembly Line. The growing competitive in automobile industry requires more effective production line with continuous running time. This demands the rollers quality to be more reliable, wear-resistance and concentricity. Roller tables can be chain driven or belt driven ( for noiseless and clean operation) with a wide variety of rollers made from steel, stainless steel, polyurethane, etc.Easy to integrate with lifters, cross transfers, swivel table, turntables and other devices to form an integrated layout.
High performance elastomer polyurethane, choose high-end raw materials imported from the industry;

Excellent chemical resistance to solvents, petroleum products and other materials.

Working temperature (-30 deg.C to 100+ deg. C depending on formulation)

Capable of handling 1500-5000kgs

Product Applications

Conveyor

Conveyor Roller

Conveyor Line

Conveyor Roller beds

properties	standard	unit	Material description and parameters
			Loresim®		Lionmox®					Logilan®
Hardness	GB/T 531. 1- 2008	Shore A	90A	95A	75A	80A	85A	90A	95A	93A	95A
Tensile Strength	GB/T 528-2009	MPa	45	50	20	27	35	40	45	40	50
100% stretching	GB/T 528-2009	MPa	6	9	2	3	4	7	9	9	11
300% stretching strength	GB/T 528-2009	MPa	15	25	5	5	9	15	25	15	19
Elongation at break	GB/T 528-2009	%	420	400	600	580	550	500	490	550	500
Tear propagation resistance	GB/T 529-2008	kN/m	80	95	50	55	65	75	90	100	110
Abrasion loss	GB/T 9867- 2008	mm ³	35	40	35	35	35	30	30	20	33
Density	GB/T 4472- 2011	g/ cm ³	1.19	1.20	1.07	1.08	1.10	1.12	1.13	1.17	1.17
Operating Temperature	/	℃	-40~70℃		-40~70℃					-40~ 110℃
Resilience	GB/T 1681- 2009	%	40	38	64	60	58	54	49	64	61
Compression set	GB/T 7759.1- 2015	%	25	30	20	20	22	23	25	23	23